PROCESSING:

Types 316 and 316L are non-hardenable by heat treatment. Annealing: Heat to 1900 – 2100°F then rapidly quench Forming: Types 316 and 316L can be readily formed and drawn.

stainless steel coil 316s

WELDING:

These alloys are generally considered to have poorer weldability than Types 304 and 304L. A major difference is the higher nickel content for these alloys which requires slower arc welding speed and more care to avoid hot cracking. When filler is needed, AWS E/ER 316L and 16-8-2 are most often specified.

316-stainless-steel-coils

Stainless Steel 316 / 316L Coils Specifications:

Specifications	ASTM A240, ASME SA240
Standard	JIS, ASTM, AISI, GB, EN, DIN
Surface	2B, BA, HL, No. 4, Mirror etc.
Finish	Cold rolled, Hot rolled
Thickness	0.3mm–100mm
Size	1000mm, 1219mm, 1250mm, 1500mm, 1524mm, 2000mm